Effect of La doping on the ferroic order in Pb-based perovskite-type relaxor ferroelectrics
Maier, B. J.
Welsch, A. M.
Angel, R. J.
Engel, J. M.
Marshall, W. G.
MetadataShow full item record
The structural alteration induced by the substitution of three-valent cations with an isotropic electronic outermost shell for Pb2+ in perovskite-type relaxors was investigated in the solid solutions Pb1-xLaxSc(1+x)/2Ta(1-x)/2O3, x = 0.08 (PST-La) and Pb1-xLaxSc(1+x)/2Nb(1-x)/2O3, x = 0.23 (PSN-La). In order to distinguish the "charge" effects from "strain" effects associated with the incorporation of La3+ in the structure, Sr-containing PbSc0.5Nb0.5O3 was characterized as well. The structure of the compounds was analyzed by in situ Raman spectroscopy, single-crystal x-ray diffraction, and powder neutron diffraction at different temperatures or pressures. It is shown that the embedding of La3+ strongly affects the ferroic structural species due to strain effects through a disturbance of the system of lone-pair electrons associated with Pb2+ and a decrease in the tolerance factor. La doping suppresses the dynamical coupling between off-centered Pb and B-site cations and enhances antiphase BO6 octahedral tilting which, depending on the level of doping, may lead to long-range order of antiphase BO6 tilts at ambient conditions and frustrated antiferroelectric order of Pb ions at low temperatures.