dc.description.abstractPorous silica-based nanocomposites are promising ceramics, as they exhibit high specific surface area, highly porous network, and a surface that can be easily functionalized. This dissertation describes the results of a study on the formation and properties of porous silica nanoparticle-based composites, using techniques of freeze casting and sintering. Kaolinite platelets and silica nanorods were added into the nanoparticle system, and their effects on modifying the porous microstructures and physical properties were investigated. During freeze casting, homogeneous microstructures with highly interconnected porosity are fabricated. Kaolinite addition results in large and more interconnected pores, while added silica nanorods cause a pore morphology evolution from circular to elongated spherical pores with increasing aspect ratio. The specific surface areas (area/mass) of the particles are conserved during freeze casting and values for the resulting composites can be accurately predicted using the area and mass of the components assuming conservation of area. Both kaolinite platelets and silica nanorods effectively improved the strength of the freeze cast green composites as they distribute any applied stress over a larger portion of the sample. Upon sintering, added kaolinite is found to modify the sintering behavior of the silica nanoparticles and a transitioning interfacial phase is identified when sintering temperature is above 1250 °C. This new phase contributes to the further enhancement of strength and this strengthening effect depends on composition and initial solids loading. After sintering at 1250 °C for 1 h, a ceramic containing 10 vol% kaolinite and 8 vol% silica has a maximum strength while maintaining a ~69% porosity. The kaolinite-silica composites with lower solids loading exhibit faster sintering (e.g. larger shrinkage, more extensive thickening of the pore walls), which, in turn, results in a rapid increase in mechanical strength. Based on the understanding of the composite properties and the underlying principles, a novel method for creating nanocomposites with precisely controllable specific surface area is developed. With repeated nanoparticle suspension infiltration, freeze drying, and sintering, the specific surface area can be varied from less than one to well over 100 m2/g, demonstrating potential application as liquid membranes.en_US
dc.publisherVirginia Techen_US
dc.relation.haspartLi_W_D_2012.pdfen_US
dc.relation.haspartLi_W_D_2012_copyright.pdfen_US
dc.rightsI hereby certify that, if appropriate, I have obtained and attached hereto a written permission statement from the owner(s) of each third party copyrighted matter to be included in my thesis, dissertation, or project report, allowing distribution as specified below. I certify that the version I submitted is the same as that approved by my advisory committee. I hereby grant to Virginia Tech or its agents the non-exclusive license to archive and make accessible, under the conditions specified below, my thesis, dissertation, or project report in whole or in part in all forms of media, now or hereafter known. I retain all other ownership rights to the copyright of the thesis, dissertation or project report. I also retain the right to use in future works (such as articles or books) all or part of this thesis, dissertation, or project report.en_US
dc.subjectSilicaen_US
dc.subjectKaoliniteen_US
dc.subjectFreeze castingen_US
dc.subjectPorous microstructureen_US
dc.subjectStrengthen_US
dc.titleStudy of Freeze-Cast Porous Silica Nanoparticle-Based Compositesen_US
dc.typedissertationen_US
dc.contributor.departmentMaterials Science and Engineeringen_US
thesis.degree.namePhDen_US
thesis.degree.leveldoctoralen_US
thesis.degree.grantorVirginia Polytechnic Institute and State Universityen_US
dc.contributor.committeechairLu, P. Kathyen_US
dc.contributor.committeememberLu, Guo-Quanen_US
dc.contributor.committeememberDucker, William A.en_US
dc.identifier.sourceurlhttp://scholar.lib.vt.edu/theses/available/etd-07112012-170112/en_US
dc.contributor.committeecochairWalz, John Y.en_US


Files in this item

Thumbnail
Thumbnail

This item appears in the following Collection(s)

Show simple item record