dc.description.abstractThe corrosion of the drinking water distribution system is a serious problem in the United States. The annual cost to repair damages related to corrosion for public utilities in the United States are estimated at $22 billion. Polyurethane can be used as an in situ pipe liner which reduces the overall cost to rehabilitate water mains. Polyurethane is gaining popularity as a drinking water pipe liner. Not much is known about the effects of polyurethane to reline potable pipes. Polyurethane has only recently begun to be approved by the U.S. Environmental Protection Agency for use in drinking water piping, although it has been used in the United Kingdom since 1999. The American National Standards Institute/National Sanitation Foundation 61 Drinking Water System Components â Health Effects (ANSI/NSF 61) for pipe and pipe liners was used to investigate changes in water quality in contact with polyurethane lining material. In addition, the exposure time was extended to 30 days and odor analysis was performed. Polyurethane coupons were placed in headspace free borosilicate glass vessels with a surface area to volume ratio of 0.39. The water was pH 8 and comprised of salts: MgSO₄, NaHCO₃, CaSO₄, CaC1₂, Na₂SiO₃ and KNO₃ in a ratio typical of standard drinking water. Three types of disinfectant were used: no disinfectant, chlorine and monochloramine. The water was removed, sampled and replaced on days 1, 2, 4, 9, 11, 14, 15, 19, 21 and 30. The sample water was tested for pH, temperature, total organic carbon concentration (TOC), disinfectant residual, ammonia concentration as N-NH₃, hardness as combined Ca and Mg concentrations, alkalinity and temperature on days when the sample water was changed. Total solids (TS), odor, trihalomethanes (THMs), haloacetic acids (HAAs), and semivolatile organic carbons (SVOCs) were tested on days 1, 4, 9, and 14. The polyurethane lining had major impacts on pH, odor and haloacetic acids throughout the 30 day experiment. A 2-3 pH unit decrease to pH 6 was constant for all conditions tested. Odor panelists described the odor for both chlorinated and monochloraminated waters as "chlorinous" and either pleasant as "sweet chemical" or putrid as "locker room" . Haloacetic acids were formed and increased in concentration (by approximately 30 µg/L, which is half the US EPA regulated value of 60 µg/L). Trihalomethane formation was not seen. Total organic carbon leached from the polyurethane liners reached 0.65 mg/L above background on day 1 but by day 15 was only >0.1 mg/L above background. Chlorine and monochloramine were consumed by the polyurethane and increased exposure time leads to decreased disinfectant residual. It is important for water utilities to know how a lining material will affect the water quality. It has been shown that other polymeric lining materials have impacted the disinfection by-products as well as producing odor. Water treatment facilities are responsible for the water quality throughout the infrastructure and with Environmental Protection Agency regulations becoming stricter they cannot afford to not know the impact of polymeric lining materials in their system.en_US
dc.publisherVirginia Techen_US
dc.relation.haspartHeather.Johnson.Masters.Thesis.pdfen_US
dc.relation.haspartHeather.Johnson.Masters.Thesis2.pdfen_US
dc.rightsI hereby certify that, if appropriate, I have obtained and attached hereto a written permission statement from the owner(s) of each third party copyrighted matter to be included in my thesis, dissertation, or project report, allowing distribution as specified below. I certify that the version I submitted is the same as that approved by my advisory committee. I hereby grant to Virginia Tech or its agents the non-exclusive license to archive and make accessible, under the conditions specified below, my thesis, dissertation, or project report in whole or in part in all forms of media, now or hereafter known. I retain all other ownership rights to the copyright of the thesis, dissertation or project report. I also retain the right to use in future works (such as articles or books) all or part of this thesis, dissertation, or project report.en_US
dc.subjectPipe Lining Materialen_US
dc.subjectWater Qualityen_US
dc.subjectDrinking Wateren_US
dc.subjectPolyurethaneen_US
dc.titleDetermination of the Influence of Polyurethane Lining on Potable Water Qualityen_US
dc.typeThesisen_US
dc.contributor.departmentEnvironmental Engineeringen_US
dc.description.degreeMaster of Scienceen_US
thesis.degree.nameMaster of Engineeringen_US
thesis.degree.levelmastersen_US
thesis.degree.grantorVirginia Polytechnic Institute and State Universityen_US
thesis.degree.disciplineEnvironmental Planningen_US
dc.contributor.committeechairDietrich, Andrea M.en_US
dc.contributor.committeememberEdwards, Marc A.en_US
dc.contributor.committeememberMarr, Linsey C.en_US
dc.identifier.sourceurlhttp://scholar.lib.vt.edu/theses/available/etd-02192009-164341/en_US
dc.date.sdate2009-02-19en_US
dc.date.rdate2009-03-06
dc.date.adate2009-03-06en_US


Files in this item

Thumbnail
Thumbnail

This item appears in the following Collection(s)

Show simple item record