    Alkali attack of coal gasifier refractory lining

    Thumbnail
    View/Open
    LD5655.V855_1987.G467.pdf (1.454Mb)
    Downloads: 394
    Date
    1987-05-15
    Author
    Gentile, Maria
    Metadata
    Show full item record
    Abstract
    An experimental test system was designed to simulate the operating conditions found in nonslagging coal gasifiers. The reaction products that form when refractory linings in coal gasifiers are exposed to alkali impurities (sodium or potassium) were experimentally determined. Analysis of selected physical and chemical properties of the reaction products, which typically form between the alkali and the refractory will lead to a better understanding of the mechanisms behind refractory failures associated with alkali attack. The reaction products sodium aluminate (Na₂O·Al₂O₃), N₂C₃A₅ (2Na₂O·3CaO·5A1₂O₃), nepheline (Na₂0·Al₂0₃·2SiO₂), potassium aluminate, (K₂Oâ·Al₂0₃), and kaliophilite (K₂O·Al₂0₃·2Si0₂) were synthesized and their solubility in water and coefficients of linear thermal expansion were: measured. Of the compounds tested, the formation of potassium aluminate would be the most detrimental to the gasifier lining. The linear thermal expansion of potassium aluminate was 2.05% from room temperature to 800°C, which was twice as large as the other compounds. Potassium aluminate also possessed the highest solubility in water which was 8.893/L at 90°C.
    URI
    http://hdl.handle.net/10919/45668
    Collections
    • Masters Theses [21549]

    If you believe that any material in VTechWorks should be removed, please see our policy and procedure for Requesting that Material be Amended or Removed. All takedown requests will be promptly acknowledged and investigated.

    Virginia Tech | University Libraries | Contact Us
     

     

    VTechWorks

    AboutPoliciesHelp

    Browse

    All of VTechWorksCommunities & CollectionsBy Issue DateAuthorsTitlesSubjectsThis CollectionBy Issue DateAuthorsTitlesSubjects

    My Account

    Log inRegister

    Statistics

    View Usage Statistics

    If you believe that any material in VTechWorks should be removed, please see our policy and procedure for Requesting that Material be Amended or Removed. All takedown requests will be promptly acknowledged and investigated.

    Virginia Tech | University Libraries | Contact Us