Ultrahigh electromechanical response in (1-x)(Na0.5Bi0.5)TiO3-xBaTiO(3) single-crystals via polarization extension

Abstract

The dielectric, ferroelectric, and electric field-induced strain response of [001]-and [101]-oriented 0.944Na(0.5)Bi(0.5)TiO(3)-0.056BaTiO(3) (0.944NBT-0.056BT) single crystals were investigated as a function of temperature and dc bias (E). An ultrahigh electromechanical response with large amplitude longitudinal piezoelectric coefficients as high as d(33)=2500 pm/V was found in 001 oriented 0.944NBT-0.056BT single crystals near a depolarization temperature of T-d = 130 degrees C. In-situ XRD revealed that the enhanced piezoelectric properties resulted from a polarization extension between a polar pseudocubic phase with a slight tetragonal (P4bm) distortion and a polar tetragonal one with a large tetragonal distortion of c/a = 1.02. Our findings indicate a potential approach to high performance lead-free piezoelectrics, via polarization extension. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4709619]

Description
Keywords
Photonic crystals, Polarization, X-ray diffraction, Piezoelectric materials, Single crystals
Citation
Ge, Wenwei, Luo, Chengtao, Zhang, Qinhui, Devreugd, Chris P., Ren, Yang, Li, Jiefang, Luo, Haosu, Viehland, D. (2012). Ultrahigh electromechanical response in (1-x)(Na0.5Bi0.5)TiO3-xBaTiO(3) single-crystals via polarization extension. Journal of Applied Physics, 111(9). doi: 10.1063/1.4709619