    Thermoelectric properties of DC-sputtered filled skutterudite thin film

    Thumbnail
    View/Open
    2015_Fu_et_al.pdf (1.706Mb)
    Downloads: 1263
    Date
    2015-03-28
    Author
    Fu, Gaosheng
    Zuo, Lei
    Chen, Jie
    Lu, Ming
    Yu, Liangyao
    Metadata
    Show full item record
    Abstract
    The Yb filled CoSb3 skutterudite thermoelectric thin films were prepared by DC magnetron sputtering. The electrical conductivity, Seebeck coefficient, thermal conductivity, and figure of merit ZT of the samples are characterized in a temperature range of 300K to 700 K. X-ray diffraction, scanning electron microscopy, and energy-dispersive X-ray spectroscopy are obtained to assess the phase composition and crystallinity of thin film samples at different heat treatment temperatures. Carrier concentrations and Hall mobilities are obtained from Hall Effect measurements, which provide further insight into the electrical conductivity and Seebeck coefficient mechanisms. The thermal conductivity of thin film filled skutterudite was found to be much less compared with bulk Yb filled CoSb3 skutterudite. In this work, the 1020K heat treatment was adopted for thin film post process due to the high degree of crystallinity as well as avoiding reverse heating effect. Thin film samples of different thicknesses were prepared with the same sputtering deposition rate and maximum ZT of 0.48 was achieved at 700K for the 130 nm thick sample. This value was between half and one third of the bulk figure of merit which was due to the lower Hall mobility. (C) 2015 AIP Publishing LLC.
    URI
    http://hdl.handle.net/10919/52617
    Collections
    • Scholarly Works, Department of Mechanical Engineering [416]

    If you believe that any material in VTechWorks should be removed, please see our policy and procedure for Requesting that Material be Amended or Removed. All takedown requests will be promptly acknowledged and investigated.

    Virginia Tech | University Libraries | Contact Us
     

     

    VTechWorks

    AboutPoliciesHelp

    Browse

    All of VTechWorksCommunities & CollectionsBy Issue DateAuthorsTitlesSubjectsThis CollectionBy Issue DateAuthorsTitlesSubjects

    My Account

    Log inRegister

    Statistics

    View Usage Statistics

    If you believe that any material in VTechWorks should be removed, please see our policy and procedure for Requesting that Material be Amended or Removed. All takedown requests will be promptly acknowledged and investigated.

    Virginia Tech | University Libraries | Contact Us