Creep and Elevated Temperature Mechanical Properties of 5083 and 6061 Aluminum
Allen, Benjamin William
MetadataShow full item record
With the increasing use of aluminum in naval vessels and the ever-present danger of fires, it is important to have a good understanding of the behavior of aluminum at elevated temperatures. The aluminum samples 5083-H116 and 6061-T651 were examined under a variety of loading conditions and temperatures. Tensile testing was completed on both materials to measure strength properties of elastic modulus, yield strength, and ultimate strength as well as reduction of area from room temperature to 500 deg C taking measurements every 50 deg C. These tests showed how much the material weakened as temperature increases. Low temperatures had a minimal effect on strength while exposure to temperatures between 200 and 300 deg C had the most significant impact. Creep testing was also completed for these materials. These tests were completed at temperatures between 200 and 400 deg C in 50 deg C increments. Stresses for these tests were in the range of 13 to 160MPa for 5083 aluminum and between 13 to 220MPa for 6061 aluminum. These tests showed a significant relationship between stress and temperature and how changes to one can cause a very different resulting behavior. In addition to the creep testing, three creep models were examined as a means of predicting creep behavior. These models included a power law, exponential, and hyperbolic-sine versions and were able to predict creep results with decent accuracy depending on the stress used in the model.
- Masters Theses