    Temperature Dependent Behavior of Optical Loss from Hydrogen Species in Optical Fibers at High Temperature

    Thumbnail
    View/Open
    etd-05202015-113311_Bonnell_EA_T_2015_3.pdf (2.543Mb)
    Downloads: 730
    etd-05202015-113311_Bonnell_EA_T_permissions_3.pdf (1.237Mb)
    Downloads: 98
    Date
    2015-04-07
    Author
    Bonnell, Elizabeth Ann
    Metadata
    Show full item record
    Abstract
    This study reports on the behavior of silica based optical fibers in a hydrogen environment at high temperatures. The hydrogen response in the form of optical loss in the wavelength range of 1000-2500 nm of a germanium doped graded index 50/125 graded index fiber was examined in the temperature range of 20–800 °C. When the fiber was exposed to hydrogen at 800 °C two absorption bands appeared: ~1390 nm assigned to the first overtone of the hydroxyl stretch and ~2200 nm band with complex assignments including the combination mode of the fundamental hydroxyl stretch with SiO4 tetrahedral vibrations and the combination mode of SiOH bend and stretch. The growth rate of the 1390 nm band fits the solution to the diffusion equation in cylindrical coordinates while the 2200 nm band does not. Absorption for both bands persisted as the fiber is cooled to room temperature. Temperature dependent behavior was observed in that as temperature increases from room temperature, the absorption intensity decreases and band shifts slightly to longer wavelengths. Temperature dependence is repeatable and reversible. However, if no hydrogen is present in the environment at temperatures greater than 700 °C, the 1390 nm band will permanently decrease in intensity, while the 2200 nm band does not change. Changes in the structure of the glass appear to be causing this temperature dependent behavior. Other necessary conditions for structural changes to cause this temperature dependent behavior are examined.
    URI
    http://hdl.handle.net/10919/78132
    Collections
    • Masters Theses [21534]

    If you believe that any material in VTechWorks should be removed, please see our policy and procedure for Requesting that Material be Amended or Removed. All takedown requests will be promptly acknowledged and investigated.

    Virginia Tech | University Libraries | Contact Us
     

     

    VTechWorks

    AboutPoliciesHelp

    Browse

    All of VTechWorksCommunities & CollectionsBy Issue DateAuthorsTitlesSubjectsThis CollectionBy Issue DateAuthorsTitlesSubjects

    My Account

    Log inRegister

    Statistics

    View Usage Statistics

    If you believe that any material in VTechWorks should be removed, please see our policy and procedure for Requesting that Material be Amended or Removed. All takedown requests will be promptly acknowledged and investigated.

    Virginia Tech | University Libraries | Contact Us