Chen, Tianran2021-05-222021-05-222021-05-21vt_gsexam:31027http://hdl.handle.net/10919/103439The application of glass fiber reinforced composites has grown rapidly due to their high strength-to-weight ratio, low cost, and chemical resistance. However, the increasing demand for fiber reinforced composites results in the generation of more composite wastes. Mechanical recycling is a cost-effective and environmentally-friendly recycling method, but the loss in the quality of recycled glass or carbon fiber composite hinders the wide-spread use of this recycling method. It is important to develop novel composite materials with higher recyclability. Thermotropic liquid crystalline polymers (TLCPs) are high-performance engineering thermoplastics, which have comparable mechanical performance to that of glass fiber. The TLCP reinforced composites, called in situ composites, can form the reinforcing TLCP fibrils during processing avoiding the fiber breakage problem. The first part of this dissertation is to study the influence of mechanical recycling on the properties of injection molded TLCP and glass fiber (GF) reinforced polypropylene (PP). The processing temperature of the injection molding process was optimized using a differential scanning calorimeter (DSC) and a rheometer to minimize the thermal degradation of PP. The TLCP and GF reinforced PP materials were mechanically recycled up to three times by repeated injection molding and grinding. The mechanical recycling had almost no influence on the mechanical, thermal, and thermo-mechanical properties of TLCP/PP because of the regeneration of TLCP fibrils during the mold filling process. On the other hand, glass fiber/PP composites decreased 30% in tensile strength and 5% in tensile modulus after three reprocessing cycles. The micro-mechanical modeling demonstrated the deterioration in mechanical properties of GF/PP was mainly attributed to the fiber breakage that occurred during compounding and grinding. The second part of this dissertation is concerned with the development of recyclable and light weight hybrid composites through the use of TLCP and glass fiber. Rheological tests were used to determine the optimal processing temperature of the injection molding process. At this processing temperature, the thermal degradation of matrix material was mitigated and the processability of the hybrid composite was improved. The best formulation of TLCP and glass fiber in the composite was determined giving rise to the generation of a recyclable hybrid composite with low melt viscosity, low mechanical anisotropy, and improved mechanical properties. Finally, TLCP reinforced polyamide composites were utilized in an additive manufacturing application. The method of selecting the processing temperature to blend TLCP and polyamide in the dual extrusion process was devised using rheological analyses to take advantage of the supercooling behavior of TLCP and minimize the thermal degradation of the matrix polymer. The composite filament prepared by dual extrusion was printed and the printing temperature of the composite filament that led to the highest mechanical properties was determined. Although the tensile strength of the TLCP composite was lower than the glass fiber or carbon fiber composites, the tensile modulus of 3D printed 60 wt% TLCP reinforced polyamide was comparable to traditional glass or carbon fiber reinforced composites in 3D printing.ETDIn Copyrightrecyclingthermotropic liquid crystalline polymerglass fibershybrid compositeadditive manufacturingpolymer compositeGeneration of Recyclable Liquid Crystalline Polymer Reinforced Composites for Use in Conventional and Additive Manufacturing ProcessesDissertation