Yang, ShuoHeyl, HannaHoma, Daniel S.Pickrell, Gary R.Wang, Anbo2020-01-242020-01-242020-01-15Yang, S.; Heyl, H.; Homa, D.; Pickrell, G.; Wang, A. Powder-in-Tube Reactive Molten-Core Fabrication of Glass-Clad BaO-TiO2-SiO2 Glass–Ceramic Fibers. Materials 2020, 13, 395.http://hdl.handle.net/10919/96575In this paper we report the fabrication of glass-clad BaO-TiO₂-SiO₂ (BTS) glass–ceramic fibers by powder-in-tube reactive molten-core drawing and successive isothermal heat treatment. Upon drawing, the inserted raw powder materials in the fused silica tubing melt and react with the fused silica tubing (housing tubing) via dissolution and diffusion interactions. During the drawing process, the fused silica tubing not only serves as a reactive crucible, but also as a fiber cladding layer. The formation of the BTS glass–ceramic structure in the core was verified by micro-Raman spectroscopy after the successive isothermal heat treatment. Second-harmonic generation and blue-white photoluminescence were observed in the fiber using 1064 nm and 266 nm picosecond laser irradiation, respectively. Therefore, the BTS glass–ceramic fiber is a promising candidate for all fiber based second-order nonlinear and photoluminescence applications. Moreover, the powder-in-tube reactive molten core method offers a more efficient and intrinsic contamination-free approach to fabricate glass–ceramic fibers.application/pdfenCreative Commons Attribution 4.0 Internationalthermal drawingmolten core fabricationglass–ceramic fibersecond-order harmonic generationphotoluminescenceArticle - Refereed2020-01-23https://doi.org/10.3390/ma13020395