Shakhatreh, Abdulsalam Ismail2022-09-152022-09-152022-09-14vt_gsexam:35471http://hdl.handle.net/10919/111833Chloride-induced stress corrosion cracking (CISCC) has been identified as the main degradation mechanism for spent nuclear fuel dry storage canisters. This type of induced cracking is complex and depends on several factors, such as material composition, exposure temperature, relative humidity, applied tensile stress, and atmospheric salt concentration. An accelerated experiment was designed to simulate marine environments in a controlled fogging chamber to examine 304 and 304L stainless steel U-bend and welded U-bend samples. The samples were exposed to chloride rich and humid fogging in a corrosion chamber at 35℃ continuously for 4 weeks, 8 weeks, and 12 weeks. The same experiment was repeated at 50℃ for 4 weeks, 8 weeks, and 14 weeks to study the sensitivity of CISCC to temperature changes. A qualitative evaluation of optical micrographs from a 3D Surface Profiler was performed for 16 corroded samples and compared with 2 reference samples. Cracking was observed on 12 out of 16 samples exposed to 35℃ and 50℃ for durations ranging from 8 to 14 weeks. Likely cracking observations were noted on 4 out of 16 samples. A quantitative statistical analysis was also performed using surface profile depth (valley) data from corroded and reference samples. The quantitative analysis examined the effect of temperature, welding, exposure duration, and material composition. The quantitative results were compared with the qualitative results and literature published in CISCC.ETDenCreative Commons Attribution 4.0 Internationalchloride-induced stress corrosion crackingstress corrosion crackingspent nuclear fuel dry storageCISCCSCCISFSIThesis