Virginia TechYan, YongkeWang, Yu. U.Priya, Shashank2014-01-212014-01-212012-05-01Yan, Yongke; Wang, Yu U.; Priya, Shashank, "Electromechanical behavior of 001 -textured Pb(Mg1/3Nb2/3)O-3-PbTiO3 ceramics," Appl. Phys. Lett. 100, 192905 (2012); http://dx.doi.org/10.1063/1.47125630003-6951http://hdl.handle.net/10919/24955[001]-textured Pb(Mg1/3Nb2/3)O-3-PbTiO3 (PMN-PT) ceramics were synthesized by using templated grain growth method. Significantly high [001] texture degree corresponding to 0.98 Lotgering factor was achieved at 1 vol. % BaTiO3 template. Electromechanical properties for [001]-textured PMN-PT ceramics with 1 vol. % BaTiO3 were found to be d(33) = 1000 pC/N, d(31) = 371 pC/N, epsilon(r) 2591, and tan delta = similar to 0.6%. Elastoelectric composite based modeling results showed that higher volume fraction of template reduces the overall dielectric constant and thus has adverse effect on the piezoelectric response. Clamping effect was modeled by deriving the changes in free energy as a function of applied electric field and microstructural boundary condition. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4712563]application/pdfen-USIn CopyrightTemplated grain-growthCeramicsPiezoelectric propertiesSingle crystalsHigh-strainPhysicsElectromechanical behavior of 001 -textured Pb(Mg1/3Nb2/3)O-3-PbTiO3 ceramicsArticle - Refereedhttp://scitation.aip.org/content/aip/journal/apl/100/19/10.1063/1.4712563Applied Physics Lettershttps://doi.org/10.1063/1.4712563