Huang, Jiang2014-03-142014-03-141995-08-05etd-11102005-141118http://hdl.handle.net/10919/40312This dissertation discusses results of crystallization kinetic, morphology and scattering studies on miscible semi crystalline blends of poly(pivalolactone)/ poly(vinylidene fluoride)(pPVLIPVF₂) and poly(pivalolactone)/poly(vinylidene fluoride <i>co</i>- tetrafluoroethylene)(95-5) (PPVL/P(VF2-TFE)(95-5)) prepared by solution blending. The spherulitic growth rates of the α-phase PPVL from miscible blends with PVF₂ or P(VF₂- TFE)(95-5) were measured by polarized optical microscopy as a function of blend composition and isothermal crystallization temperature, Tx, between 160°C and 215.5°C. The PPVL weight fraction in the blends ranged from 100 to 10 wt%. Using the Lauritzen-Hoffman kinetic theory of polymer crystal growth, the equilibrium melting temperatures of the α-phase PPVL in both the PPVL/PVF₂ and the PPVL/P(VF₂-TFE)(95-5) blends have been determined, for the first time, directly from the spherulitic growth rate data. Analysis of the composition dependence of the nucleation constant, Kg suggests that the α-phase PPVL crystal/melt lateral interface free energy, Ï , in the blends decreases markedly with increasing PVF₂ or P(VF₂-TFE)(95-5) concentration.xiii, 167 leavesBTDapplication/pdfenIn CopyrightMiscible Polymer BlendsPoly(vinylidenc fluoride)Poly(pivalolactone)LD5655.V856 1995.H835Dissertationhttp://scholar.lib.vt.edu/theses/available/etd-11102005-141118/