Lohneis, Taylor Paige2019-12-052019-12-052019-12-04vt_gsexam:22761http://hdl.handle.net/10919/95943Nanotechnology and its potential for biomedical applications has become an area of increasing interest over the last few decades. Specifically, ultrasmall nanoparticles, ranging in size from 5 to 50 nm, are highly sought after for their physical and chemical properties and their ability to be easily transmitted though the bloodstream. By adjusting the material properties, size, surface potential, morphology, surface modifications, and more, of nanoparticles, it is possible to tailor them to a specific use in biomedical areas such as drug and gene delivery, biodetection of pathogens or proteins, and tissue engineering. The aim of this study was to fabricate ultrasmall poly-(lactic-co-glycolic acid) nanoparticles (PLGA NPs) using a quick and easy nanoprecipitation method1, with some modifications, for general use in various biomedical areas. Nanoprecipitation of two solutions – PLGA dissolved in acetonitrile and aqueous poly(vinyl alcohol) (PVA) – at varying concentrations produced ultrasmall nanoparticles that range in size, on average, from 10 to 30 nm. By the data collected from this study, a selection method can be used to choose a desired PLGA nanoparticle size given a potential biomedical application. The desired nanoparticle can be fabricated using specific concentrations of the two nanoprecipitation solutions. Size of the ultrasmall PLGA NPs was characterized by dynamic light scattering (DLS) and confirmed by transmission electron microscopy (TEM). Spherical morphology of the PLGA NPs was also proved by TEM. By generalizing the ultrasmall PLGA NP fabrication process, the idea is that these NPs will be able to be used in various biomedical applications depending on the goal of the furthered study. As an example of potential application, ~15 to 20 nm PLGA NPs were consistently fabricated for use as virus-like particle (VLP) scaffolds. Following formation, PLGA NPs were introduced to modified human papillomavirus (HPV) protein during protein refolding and assembly into virus-like particles (VLPs) via buffer exchange. The size of the VLPs was monitored with and without PLGA nanoparticles present in solution during the refolding process and TEM images were collected to confirm encapsulation.ETDIn CopyrightPLGA nanoparticlesultrasmall sizenanoprecipitationvirus-like particlesprotein-based vaccinesprotein assemblyVLP scaffoldThesis