VTechWorks staff will be away for the Thanksgiving holiday beginning at noon on Wednesday, November 27, through Friday, November 29. We will resume normal operations on Monday, December 2. Thank you for your patience.

Browsing by Author "Kosoglu, Mehmet Alpaslan"

Now showing 1 - 2 of 2
  • Thumbnail Image
    Fiber array for optical imaging and therapeutics
    (United States Patent and Trademark Office, 2014-08-05)
    The present invention relates to the field of optical imaging and therapeutics. More particularly, embodiments of the present invention provide minimally-invasive Fiberoptic Microneedle Devices (FMDs) for light-based therapeutics, which physically penetrate tissue and deliver light directly into the target area below the skin surface (FIG. 1). A preferred embodiment of the invention is a fiberoptic microneedle device comprising: (a) one or more silica-based needles capable of guiding light and comprising a length of about 0.5-6 mm, a base having an outer diameter in the range of about 100-150 micron, and a tip having an outer diameter in the range of about 5-20 micron; (b) a support member to which the needles are secured; (c) a ferrule comprising one or more holes for each of the needles, wherein the ferrule is operably configured to provide mechanical support to each needle at all or some portion of the length of the needle. Embodiments of the invention enable depth-selective and deep photothermal therapeutics and can be adapted for use with any laser-based treatment or diagnostic in which light is used to detect or treat targets under or on the skin surface.
  • Thumbnail Image
    Fiberoptic Microneedles for Transdermal Light Delivery
    Kosoglu, Mehmet Alpaslan (Virginia Tech, 2011-10-19)
    Shallow light penetration in tissue has been a technical barrier to the development of photothermal therapies for cancers in the epithelial tissues and skin. This problem can potentially be solved by utilizing minimally invasive probes to deliver light directly to target areas potentially > 2 mm deep within tissue. To develop this solution, fiber optic microneedles capable of delivering light for therapy were manufactured. We have manufactured fiberoptic microneedles by tapering silica-based optical fibers employing a melt-drawing process. These fiberoptic microneedles were 35 to 139 microns in diameter and 3 mm long. Some of the microneedles were manufactured to have sharper tips (tip diameter < 8 microns) by changing the heat source during the melt-drawing process. All of the microneedles were individually inserted into ex vivo porcine skin samples to demonstrate the feasibility of their application in human tissues. Skin penetration experiments showed that sharp fiber optic microneedles with a minimum average diameter of 73 microns and a maximum tip diameter of 8 microns were able to penetrate skin without buckling. Flat microneedles, which had larger tip diameters, required a minimum average diameter of 125 microns in order to penetrate through porcine skin samples. Force versus displacement plots showed that a sharp tip on a fiber optic microneedle decreased the skin's resistance during insertion. Also, the force acting on a sharp microneedle increased more steadily compared with a microneedle with a flat tip. Melt-drawn fiberoptic microneedles provided a means to mechanically penetrate dermal tissue and deliver light directly into a localized target area. We also described an alternate fiberoptic microneedle design with the capability of delivering more diffuse, but therapeutically useful photothermal energy using hydrofluoric acid etching of optical fibers. Microneedles etched for 10, 30, and 50 minutes, and an optical fiber control was compared for their ability to deliver diffuse light using three techniques. First, red light delivery from the microneedles was evaluated by imaging the reflectance of the light from a white paper. Second, spatial temperature distribution of the paper in response to near-IR light (1,064 nm, 1 W, CW) was recorded using infrared thermography. Third, ex vivo adipose tissue response during 1,064 nm, (5 W, CW) irradiation was recorded with bright field microscopy. Increasing etching time decreased microneedle diameter (from 125 to 33 microns), resulting in increased uniformity of red and 1,064 nm light delivery along the microneedle axis. For equivalent total energy delivery, microneedles with smaller diameters reduced carbonization in the adipose tissue experiments. However, thin fiberoptic microneedles designed to minimize tissue disruption and deliver diffuse therapeutic light are limited in their possible clinical application due to a lack of mechanical strength. Fiberoptic microneedles have been embedded in an elastomeric support medium (polydimethylsiloxane, PDMS) to mitigate this issue. The critical buckling force of silica microneedles with 55, 70, and 110 microns diameters and 3 mm length were measured with and without the elastomeric support in place (N = 5). Average increases in the mechanical strength for microneedles of 55, 70, and 110 microns diameters were measured to be 610%, 290%, and 33%, respectively. Aided by mechanical strengthening through an elastomeric support, microneedles with 55 microns diameter were able to repeatedly penetrate ex vivo porcine skin.