Browsing by Author "Laborie, Marie-Pierre Genevieve"

Now showing 1 - 2 of 2
  • Thumbnail Image
    3D printing of lignin: Challenges, opportunities and roads onward
    Ebers, L. -S.; Arya, Aditi; Bowland, C. C.; Glasser, Wolfgang G.; Chmely, S. C.; Naskar, A. K.; Laborie, Marie-Pierre Genevieve (2021-06)
    As the second most abundant biopolymer on earth, and as a resource recently becoming more available in separated and purified form on an industrial scale due to the development of new isolation technologies, lignin has a key role to play in transitioning our material industry towards sustainability. Additive manufacturing (AM), the most efficient-material processing technology to date, has likewise made great strides to promote sustainable industrial solutions to our needs in engineered products. Bringing lignin research to AM has prompted the emergence of the nascent "lignin 3D printing" field. This review presents the recent state of art of this promising field and highlights its challenges and opportunities. Following a review of the industrial availability, molecular attributes, and associated properties of technical lignins, we review R&D efforts at implementing lignin systems in extrusion-based and stereolithography (SLA) printing technologies. Doing so underlines the adage of lignin research that "all lignins are not created equal," and stresses the opportunity nested in this chemical diversity created mostly by differences in isolation conditions to molecularly select and tune the attributes of technical lignin systems towards desirable properties, be it by modification or polymer blending. Considering the AM design process in its entirety, we finally propose onward routes to bring the full potential to this emerging field. We hope that this review can help promote the unique value and overdue industrial role of lignin in sustainable engineered materials and products.
  • Thumbnail Image
    Investigation of the Wood/Phenol-Formaldehyde Adhesive Interphase Morphology
    Laborie, Marie-Pierre Genevieve (Virginia Tech, 2002-02-01)
    This work addresses the morphology of the wood/ Phenol-Formaldehyde (PF) adhesive interphase using yellow-poplar. In this case, morphology refers to the scale or dimension of adhesive penetration into wood. The objective is to develop methods for revealing ever smaller levels of wood/resin morphology. Dynamic techniques that are commonly utilized in polymer blend studies are investigated as potential methods for probing the wood/ adhesive interphase morphology. These are Dynamic Mechanical Analysis (DMA) and solid state NMR using CP/MAS. PF resin molecular weight is manipulated to promote or inhibit resin penetration in wood, using a very low or a very high molecular weight PF resin. With DMA, the influence of PF resin on wood softening is investigated. It is first demonstrated that the cooperativity analysis according to the Ngai coupling model of relaxation successfully applies to the in-situ lignin glass transition of yellow-poplar and spruce woods. No significant difference in intermolecular coupling is detected between the two woods. It is then demonstrated that combining simple DMA measurements with the cooperativity analysis yields ample sensitivity to the interphase morphology. From simple DMA temperature scans, a low molecular weight PF (PF-Low) does not influence lignin glass transition temperature. However, the Ngai coupling model of relaxation indicates that intermolecular coupling is enhanced with the low molecular weight PF. This behavior is ascribed to the low molecular weight PF penetrating lignin on a nanometer scale and polymerizing in-situ. On the other hand, a high molecular weight resin with a broad distribution of olecular weights (PF-High) lowers lignin glass transition temperature dramatically. This plasticizing effect is ascribed to a small fraction of the PF resin being low enough in molecular weight to penetrate lignin on a nanoscale, but being too dispersed for forming a crosslinked network. With CP/MAS NMR, intermolecular cross-polarization experiments are found unsuitable to probe the angstrom scale morphology of the wood adhesive interphase. However, observing the influence of the PF resins on the spin lattice relaxation time in the rotating frame, HT1r, and the cross-polarization time (TCH) is useful for probing the interphase morphology. None of the resins significantly affects the cross-polarization time, suggesting that angstrom scale penetration does not occur with a low nor a high molecular weight PF resin. However, the low molecular weight PF substantially modifies wood polymer HT1r, indicating that the nanometer scale environment of wood polymers is altered. On the other hand, the high molecular weight PF resin has no effect on wood HT1r. On average, the high molecular weight PF does not penetrate wood on a nanometer scale. Interestingly, the low molecular weight PF resin disrupts the spin coupling that is typical among wood components. Spin coupling between wood components is insensitive to the high molecular weight PF. Finally, it is noteworthy that the two PF resins have significantly different T1r 's in-situ. The low molecular weight resin T1r lies within the range of wood relaxations, suggesting some degree of spin coupling. On the other hand, the T1r of the high molecular weight PF appears outside the range of wood relaxations. Spin coupling between the high molecular weight resin and wood components is therefore inefficient. The CP/MAS NMR and DMA studies converge to identify nanometer scale penetration of the low molecular weight PF in wood. On the other hand, the high molecular weight PF resin forms separate domains from wood, although a very small fraction of the PF-High is able to penetrate wood polymers on a nanoscale.