    Analysis of Deformation Fixation of Thermally Compressed Scots Pine (Pinus sylvestris L.)
    Li, Lili; Shan, Xiaofei; Luo, Zhiying; Liu, Wenwen; Liu, Jianxia; Yu, Jianfang; Chen, Zhangjing; Wang, Ximing (MDPI, 2024-05-11)
    Heat treatment effectively inhibits the water absorption recovery of compressed wood. To elucidate this phenomenon, we prepared compressed pine and thermally compressed pine (heartwood and sapwood) using the hot pressing method at 160 °C, 180 °C, 200 °C, and 220 °C. The effects of chemical components, swelling stresses, and monosaccharides on modified wood recovery were investigated using regression analyses. Notably, the recovery of both compressed heartwood and sapwood during water absorption declined from 18.89% to 2.66% and from 58.40% to 1.60%, respectively, after heat treatment. Similarly, the swelling stresses of the compressed heartwood and sapwood at 220 °C, respectively, ranged from 0.693 MPa to 0.275 MPa and from 0.783 MPa to 0.330 MPa. These were close to the values of untreated heartwood (0.175 MPa) and sapwood (0.225 MPa). Regression functions indicated that the recovery of compressed wood is chemically dependent on hemicellulose and mechanically related to swelling stress. For monosaccharides, regression functions indicated that modified heartwood recovery primarily relied on mannose, whereas modified sapwood recovery was remarkably affected by mannose and xylose. This confirmed that the pyrolytic monosaccharides in hemicellulose promoted stress relaxation, which induced the deformation fixation of thermally compressed wood.
  • Thumbnail Image
    Effects of Thermo-Hydro-Mechanical Treatments on Various Physical and Mechanical Properties of Poplar (Populus) Wood
    Shao, Yali; Li, Lili; Chen, Zhangjing; Wang, Sunguo; Wang, Ximing (2020-11)
    Poplar (Populus) wood was subjected in this work to thermo-hydro-mechanical treatment. The influence of the treatment parameters on the physical and mechanical properties were investigated. The wood samples were densified under three compression ratios (0%, 30%, and 50%), and thermally treated at three temperatures (180 degrees C, 200 degrees C, and 220 degrees C), at three thermal treatment durations (3 h, 4 h, and 5 h). The density, modulus of elasticity, modulus of rupture, radial hardness, and thickness swelling were measured. The results showed that the densities of the samples increased by 36.6% to 49.7%. As the compression rate increased, the temperature, duration, modulus of elasticity, modulus of rupture, and hardness increased. However, the dimensions of the densified samples were less stable. Compared to the densified samples, the maximum thickness swelling could be reduced by 74% (from 29.7% to 7.8%) when subjected to a thermal treatment at 220 degrees C for 3 h.