    Efficient Adsorption-Assisted Photocatalysis Degradation of Congo Red through Loading ZIF-8 on KI-Doped TiO2
    Liu, Zhechen; Zhang, Wanqi; Zhao, Xilong; Sheng, Xianliang; Hu, Zichu; Wang, Qiang; Chen, Zhangjing; Wang, Sunguo; Zhang, Xiaotao; Wang, Ximing (MDPI, 2022-04-13)
    Zeolitic imidazolate framework-8 (ZIF-8) was evenly loaded on the surface of TiO2 doped with KI, using a solvent synthesis method, in order to produce a ZIF-8@TiO2 (KI) adsorption photocatalyst with good adsorption and photocatalytic properties. The samples were characterized by XRD, SEM, EDX, XPS, BET and UV-Vis. The photocatalytic efficiency of the material was obtained by photocatalytic tests. The results indicate that the doping with I inhibited the grain growth and reduced the crystallite size of TiO2, reduced the band gap width and improved the utilization rate for light. TiO2 (KI) was a single crystal of anatase titanium dioxide. The combination of ZIF-8 and TiO2 (KI) improved the specific surface area and increased the reaction site. The ZIF-8@TiO2 (KI) for Congo red was investigated to validate its photocatalytic performance. The optimal concentration of Congo red solution was 30 mg/L, and the amount of catalyst was proportional to the degradation efficiency. The degradation efficiency of ZIF-8@TiO2 (5%KI) was 76.42%, after being recycled four times.
  • Thumbnail Image
    Enhanced heavy metal removal from an aqueous environment using an eco-friendly and sustainable adsorbent
    Zhang, Wanqi; An, Yuhong; Li, Shujing; Liu, Zhechen; Chen, Zhangjing; Ren, Yukun; Wang, Sunguo; Zhang, Xiaotao; Wang, Ximing (2020-10-05)
    Thiol-lignocellulose sodium bentonite (TLSB) nanocomposites can effectively remove heavy metals from aqueous solutions. TLSB was formed by using-SH group-modified lignocellulose as a raw material, which was intercalated into the interlayers of hierarchical sodium bentonite. Characterization of TLSB was then performed with BET, FTIR, XRD, TGA, PZC, SEM, and TEM analyses. The results indicated that thiol-lignocellulose molecules may have different influences on the physicochemical properties of sodium bentonite, and an intercalated-exfoliated structure was successfully formed. The TLSB nanocomposite was subsequently investigated to validate its adsorption and desorption capacities for the zinc subgroup ions Zn(II), Cd(II) and Hg(II). The optimum adsorption parameters were determined based on the TLSB nanocomposite dosage, concentration of zinc subgroup ions, solution pH, adsorption temperature and adsorption time. The results revealed that the maximum adsorption capacity onto TLSB was 357.29 mg/g for Zn(II), 458.32 mg/g for Cd(II) and 208.12 mg/g for Hg(II). The adsorption kinetics were explained by the pseudo-second-order model, and the adsorption isotherm conformed to the Langmuir model, implying that the dominant chemical adsorption mechanism on TLSB is monolayer coverage. Thermodynamic studies suggested that the adsorption is spontaneous and endothermic. Desorption and regeneration experiments revealed that TLSB could be desorbed with HCl to recover Zn(II) and Cd(II) and with-HNO3 to recover Hg(II) after several consecutive adsorption/desorption cycles. The adsorption mechanism was investigated through FTIR, EDX and SEM, which demonstrated that the introduction of thiol groups improved the adsorption capacity. All of these results suggested that TLSB is an eco-friendly and sustainable adsorbent for the extraction of Zn(II), Cd(II) and Hg(II) ions in aqueous media.
  • Thumbnail Image
    Eu-Doped Zeolitic Imidazolate Framework-8 Modified Mixed-Crystal TiO2 for Efficient Removal of Basic Fuchsin from Effluent
    Zhang, Wanqi; Liu, Hui; Liu, Zhechen; An, Yuhong; Zhong, Yuan; Hu, Zichu; Li, Shujing; Chen, Zhangjing; Wang, Sunguo; Sheng, Xianliang; Zhang, Xiaotao; Wang, Ximing (MDPI, 2021-11-27)
    Zeolitic imidazolate framework-8 (ZIF-8) was doped with a rare-earth metal, Eu, using a solvent synthesis method evenly on the surface of a mixed-crystal TiO2(Mc-TiO2) structure in order to produce a core–shell structure composite ZIF-8(Eu)@Mc-TiO2 adsorption photocatalyst with good adsorption and photocatalytic properties. The characterisation of ZIF-8(Eu)@Mc-TiO2 was performed via X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), Brunauer–Emmett–Teller analysis (BET) and ultraviolet–visible light differential reflectance spectroscopy (UV-DRs). The results indicated that Eu-doped ZIF-8 was formed evenly on the Mc-TiO2 surface, a core–shell structure formed and the light-response range was enhanced greatly. The ZIF-8(Eu)@Mc-TiO2 for basic fuchsin was investigated to validate its photocatalytic performance. The effect of the Eu doping amount, basic fuchsin concentration and photocatalyst dosage on the photocatalytic efficiency were investigated. The results revealed that, when 5%-Eu-doped ZIF-8(Eu)@Mc-TiO2 (20 mg) was combined with 30 mg/L basic fuchsin (100 mL) under UV irradiation for 1 h, the photocatalytic efficiency could reach 99%. Further, it exhibited a good recycling performance. Thus, it shows certain advantages in its degradation rate and repeatability compared with previously reported materials. All of these factors suggested that, in an aqueous medium, ZIF-8(Eu)@Mc-TiO2 is an eco-friendly, sustainable and efficient material for the photocatalytic degradation of basic fuchsin.