    Clearance of Biodegradable Polymer and Polyethylene Films from the Rumens of Holstein Bull Calves
    Galyon, Hailey; Vibostok, Samuel; Duncan, Jane; Ferreira, Gonzalo; Whittington, Abby; Havens, Kirk; McDevitt, Jason; Cockrum, Rebecca R. (MDPI, 2023-03-03)
    Due to the occurrence of plastic impaction in ruminants and its deleterious effects on health and production, it is necessary to determine the suitability of biodegradable polymers to replace polyethylene-based agricultural plastics, such as hay netting. The objectives of this study were to evaluate the clearance of a polyhydroxyalkanoate (PHA) and poly(butylene succinate-co-adipate) (PBSA) melt-blend polymer from the rumen when fed to cattle and subsequent animal health. Twelve Holstein bull calves were dosed with an encapsulated 13.6 g of PBSA:PHA (Blend), 13.6 g of low-density polyethylene (LDPE), or four empty gelatin capsules (Control) for 30 d. The feed intake, body weight, and body temperature were evaluated, and hemograms were run on d 0 and d 30. On d 31, calves were euthanized to evaluate gross rumen measurements and pathology, papillae length, and polymer residues in rumen contents. No calves presented any signs related to plastic impaction. The feed intake; body weight; rectal temperature; hematological parameters; gross rumen measurements and pathology; and rumen pH and temperature were not affected by treatments. Calves dosed with LDPE had 27 g of undegraded polymer retained in the rumen while Blend calves had only 2 g of fragmented polymers that were 10% of their original size. Agricultural plastics developed from PBSA:PHA may be a suitable alternative to LDPE-based products in the case of animal ingestion and may reduce the incidence of plastic impaction.
  • Thumbnail Image
    Digestibility Kinetics of Polyhydroxyalkanoate and Poly(butylene succinate-co-adipate) after In Vitro Fermentation in Rumen Fluid
    Galyon, Hailey; Vibostok, Samuel; Duncan, Jane; Ferreira, Gonzalo; Whittington, Abby; Havens, Kirk; McDevitt, Jason; Cockrum, Rebecca R. (MDPI, 2022-05-21)
    Using polyhydroxyalkanoate (PHA) materials for ruminal boluses could allow for longer sustained release of drugs and hormones that would reduce administration time and unneeded animal discomfort caused by continuous administration. The objective of this study was to determine ruminal degradability and kinetics of biodegradable polymers and blends. A proprietary PHA-based polymer, poly(butylene succinate-co-adipate) (PBSA), PBSA:PHA melt blends, and forage controls were incubated in rumen fluid for up to 240 h. Mass loss was measured after each incubation time, and digestion kinetic parameters were estimated. Thermogravimetric, differential scanning calorimetry, and intrinsic viscosity analyses were conducted on incubated samples. Generally, across treatments, mass loss was significant by 96 h with a minimum increase of 0.25% compared to 0 h but did not change thereafter. Degradation kinetics demonstrated that polymer treatments were still in the exponential degradation phase at 240 h with a maximum disappearance rate of 0.0031 %/h. Melting temperature increased, onset thermal degradation temperature decreased, and intrinsic viscosity decreased with incubation time, indicating structural changes to the polymers. Based on these preliminary findings, the first stage of degradation occurs within 24 h and PHA degrades slowly. However, further ruminal degradation studies of biodegradable polymers are warranted to elucidate maximum degradation and its characteristics.
  • Thumbnail Image
    Long-term in situ ruminal degradation of biodegradable polymers in Holstein dairy cattle
    Galyon, Hailey; Vibostok, Samuel; Duncan, Jane; Ferreira, Gonzalo; Whittington, Abby; Cockrum, Rebecca R. (American Dairy Science Association, 2022-12-22)
    Using biodegradable materials such as polyhydroxyalkanoates (PHA) and poly(butylene succinate-co-adipate) (PBSA) to develop single-use agricultural plastics like bale netting may reduce the negative effects of plastic accumulation in the rumens of cattle. The objective of this research was to assess the long-term degradation of PHA, PBSA, and a PBSA:PHA blend (Blend) compared with a low-density polyethylene (LDPE) control. Polyhydroxyalkanoate, PBSA, Blend, and LDPE films were incubated in the rumens of 3 cannulated, nonlactating Holsteins for up to 150 d. In situ disappearance (ISD) and residue length were assessed after every incubation time. Data were analyzed with PROC MIXED in SAS and adjusted by Tukey's method to determine least squares differences between polymer treatments, incubation time, and their interaction. By 30 d, PHA achieved 100% degradation, with initiation occurring at 14 d indicated by ISD and a reduction in residue length. Poly(butylene succinate-co-adipate) and Blend did not achieve any significant ISD, but fragmentation of PBSA occurred at 60 d and fragmentation of Blend at just 1 d, likely due to abiotic hydrolysis. Low-density polyethylene achieved no ISD, and residue length did not change over incubation time. We propose that a PBSA:PHA blend is a valid alternative to polyethylene single-use agricultural plastic products based on its fragmentation within 1 d of incubation.