dc.identifier.citationBrian Geist, William B. Spillman Jr., and Richard O. Claus, "Thermal cycling and the optical and electrical characterization of self-assembled multilayer Nile Blue A–gold thin films," Appl. Opt. 44, 6357-6360 (2005). doi: 10.1364/ao.44.006357
dc.identifier.issn1559-128X
dc.identifier.urihttp://hdl.handle.net/10919/46968
dc.description.abstractSome laser applications produce high power densities that can be dangerous to equipment and operators. We have fabricated thin-film coatings by using molecular electrostatic self-assembly to create a spectrally selective absorbing coating that is able to withstand thermal fluctuations from -20 degrees C to 120 degrees C. We made the thin-film coatings by alternating deposition of an organic dye and gold colloidal nanoparticles onto glass substrates. Nile Blue A perchlorate, with a maximum absorbance slightly above 632 nm, was chosen as the organic dye. Strong coupling between the dye molecules and the gold nanoparticles provides a redshift that increases as the film's thickness is increased. The incorporation of the gold colloidal nanoparticles also decreases the resistivity of the film. The resistivity of the film was measured with a four-point probe and found to be similar to 10 ohm/cm for the two samples measured. Atomic-force microscopy was used to show that film thickness increased 2.4 nm per bilayer. The optical properties of the film were measured at the end of every 5 thermal cycles from -20 degrees C to 120 degrees C, and negligible degradation was observed after 30 cycles. (c) 2005 Optical Society of America
dc.format.mimetypeapplication/pdfen_US
dc.language.isoen_US
dc.publisherOptical Society of America
dc.subjectNanoparticlesen_US
dc.subjectDYEen_US
dc.titleThermal Cycling And The Optical And Electrical Characterization Of Self-Assembled Multilayer Nile Blue A-Gold Thin Filmsen_US
dc.typeArticleen_US
dc.identifier.urlhttp://www.opticsinfobase.org/ao/abstract.cfm?URI=ao-44-30-6357
dc.date.accessed2014-02-24
dc.title.serialApplied Optics
dc.identifier.doihttps://doi.org/10.1364/ao.44.006357
dc.type.dcmitypeTexten_US


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record