    Study of mechanical alloying of Sm and Fe

    Thumbnail
    View/Open
    1997_Study_mechanical_alloying.pdf (446.3Kb)
    Downloads: 346
    Date
    1997-04-15
    Author
    Seifu, Dereje
    Oliver, Frederick W.
    Hoffman, Eugene J.
    Aning, Alex O.
    Babu, V. Suresh
    Seehra, Mohindar S.
    Catchings, Robert M.
    Metadata
    Show full item record
    Abstract
    Mechanical alloying of Sm and Fe with the composition of SmFe3 was studied using x-ray-diffraction (XRD), Mossbauer, and magnetization measurements. Data taken as a function of milling time for up to 20 h show significant changes occurring during ball milling. The XRD studies show that the initial crystalline Bragg reflections changed to a broad maximum, which is attributed to the formation of an amorphous phase. The initial six-line pattern in the Mossbauer spectrum, characteristic of magnetic ordering, changed to a broad singlet, characteristic of a nonmagnetic material. Magnetization measurements revealed that the coercive field was at its maximum after 5 h of milling and decreased sharply as the milling time increased. The remanent magnetization was at its maximum between 5 and 10 h of milling. The final product of the ball milling, which exhibited the characteristics of an amorphous paramagnetic material in its XRD and Mossbauer spectrum, was studied after heat treatment. The XRD and the Mossbauer spectra of the heat treated alloy show that substantial changes occurred during heat treatment in that sharp Bragg reflections, characteristic of crystalline materials, reappear and the alloy changed from a paramagnetic to a ferromagnetic state. (C) 1997 American Institute of Physics.
    URI
    http://hdl.handle.net/10919/52476
    Collections
    • Scholarly Works, Materials Science and Engineering (MSE) [398]

    If you believe that any material in VTechWorks should be removed, please see our policy and procedure for Requesting that Material be Amended or Removed. All takedown requests will be promptly acknowledged and investigated.

    Virginia Tech | University Libraries | Contact Us
     

     

    VTechWorks

    AboutPoliciesHelp

    Browse

    All of VTechWorksCommunities & CollectionsBy Issue DateAuthorsTitlesSubjectsThis CollectionBy Issue DateAuthorsTitlesSubjects

    My Account

    Log inRegister

    Statistics

    View Usage Statistics

    If you believe that any material in VTechWorks should be removed, please see our policy and procedure for Requesting that Material be Amended or Removed. All takedown requests will be promptly acknowledged and investigated.

    Virginia Tech | University Libraries | Contact Us