    Processing of Aluminum Alloys Containing Displacement Reaction Products

    Thumbnail
    View/Open
    Final_dissertation.pdf (1.628Mb)
    Downloads: 95
    Date
    1998-07-15
    Author
    Stawovy, Michael Thomas
    Metadata
    Show full item record
    Abstract
    Aluminum and metal-oxide powders were mixed using mechanical alloying. Exothermic displacement reactions could be initiated in the powders either by mechanical alloying alone or by heat treating the mechanically alloyed powders. Exponential relationships developed between the initiation time of the reaction and the mechanical alloying charge ratio. The exponential relationships were the result of changes in the intensity and quantity of collisions occurring during mechanical alloying. Differential thermal analysis of the mechanically alloyed powders indicated that increased milling time inhibited the initiation of the displacement reactions. It is believed that the reactions were inhibited because of heat dissipation from reacting oxide particles in the surrounding metal. Determining the effects of mechanical alloying on displacement reactions will lead to a more thorough understanding of the kinetics of mechanical alloying. Reacted powders were densified by uniaxial compaction and extrusion. Metallographic analysis of the reacted specimens confirmed the findings of the thermal analysis. Increased mechanical alloying inhibited the chemical reactions. Densified specimens from longer-milled mechanically alloyed specimens showed finer, more uniformly dispersed reaction products. These samples also showed increased mechanical properties as a result of their finer microstructure. Current particle strengthening models were used to accurately predict room temperature properties. Because of the fine microstructures produced, it may be possible to use similar techniques to yield new high-temperature aluminum alloys.
    URI
    http://hdl.handle.net/10919/27233
    Collections
    • Doctoral Dissertations [14965]

    If you believe that any material in VTechWorks should be removed, please see our policy and procedure for Requesting that Material be Amended or Removed. All takedown requests will be promptly acknowledged and investigated.

    Virginia Tech | University Libraries | Contact Us
     

     

    VTechWorks

    AboutPoliciesHelp

    Browse

    All of VTechWorksCommunities & CollectionsBy Issue DateAuthorsTitlesSubjectsThis CollectionBy Issue DateAuthorsTitlesSubjects

    My Account

    Log inRegister

    Statistics

    View Usage Statistics

    If you believe that any material in VTechWorks should be removed, please see our policy and procedure for Requesting that Material be Amended or Removed. All takedown requests will be promptly acknowledged and investigated.

    Virginia Tech | University Libraries | Contact Us