    Improving the Exfoliation of Layered Silicate in a Poly(ethylene terephthalate) Matrix Using Supercritical Carbon Dioxide

    Thumbnail
    View/Open
    JoeS-ETD-Edited(2).pdf (2.576Mb)
    Downloads: 237
    Date
    2008-04-29
    Author
    Samaniuk, Joseph Reese
    Metadata
    Show full item record
    Abstract
    Supercritical carbon dioxide (scCO2) was used as a processing aid to improve the level of exfoliation achievable in a PET-layered silicate nanocomposite produced from melt compounding. Layered silicate and scCO2 were allowed to mix for a period of time before being released into the second stage of a single screw extruder. The rapid expansion forced silicate particles into a modified hopper containing neat PET pellets. The mixture of layered silicate and PET was immediately melt mixed in a single screw extruder, cooled in a water bath and pelletized. Two sets of samples each containing layered silicate with different surface chemistries were produced with this method at 1, 3 and 5 wt% silicate. For comparison, samples of the same weight fraction and type of silicate were produced from a traditional melt compounding method. Wide angle x-ray diffraction (WAXD), mechanical testing and rheological analysis were used in order to characterize the silicate morphology, the composite mechanical properties and the relative amount of degradation between the various samples. Results show that scCO2 processed samples contain a higher degree of layered silicate exfoliation than samples produced with traditional melt compounding. Mechanical property improvements are shown to be dependent on the type of silicate surface modification employed. Finally, degradation of the PET matrix appears to be far less extensive in the scCO2 processed samples as shown from rheological data.
    URI
    http://hdl.handle.net/10919/32187
    Collections
    • Masters Theses [19642]

    If you believe that any material in VTechWorks should be removed, please see our policy and procedure for Requesting that Material be Amended or Removed. All takedown requests will be promptly acknowledged and investigated.

    Virginia Tech | University Libraries | Contact Us
     

     

    VTechWorks

    AboutPoliciesHelp

    Browse

    All of VTechWorksCommunities & CollectionsBy Issue DateAuthorsTitlesSubjectsThis CollectionBy Issue DateAuthorsTitlesSubjects

    My Account

    Log inRegister

    Statistics

    View Usage Statistics

    If you believe that any material in VTechWorks should be removed, please see our policy and procedure for Requesting that Material be Amended or Removed. All takedown requests will be promptly acknowledged and investigated.

    Virginia Tech | University Libraries | Contact Us