Arsenic Release from Chlorine Promoted Oxidation of Pyrite in the St. Peter Sandstone Aquifer, Eastern Wisconsin
MetadataShow full item record
Thin sections were made from aquifer material collected at Leonardâ s Michael quarry, located in Winnebago County, Wisconsin. Bulk arsenic content of this material was measured as 674 ppm. Quantitative EPMA analysis shows As zoning in pyrite grains with concentrations up to 1 wt. % As. After mineral characterization, the thin sections were exposed to solutions of 60 mg/L â free chlorine,â 1200 mg/L â free chlorine,â and nanopure water (control) at pH 7.0 and pH 8.5 for 24 hours. Thin sections were then analyzed to measure changes in the pyrite surfaces. For solution experiments, aquifer material was crushed to between 250 Î¼m and 355 Î¼m mesh sizes (S.A. ~ 50 cm2/g â 60 cm2/g, Foust et al. 1980) and reacted under the same conditions as the thin sections in a batch reactor. Solution samples were collected periodically during the 24 hour exposure and analyzed for arsenic, iron, and sulfate ion.
Pyrite oxidation is shown to dramatically increase with increasing chlorine concentrations as shown by measurements of released sulfate ion, used here as the reaction progress variable. EPMA maps also reveal complete oxidation of pyrite cements to Fe-oxyhydroxides at 1200 mg/L â free chlorineâ and pH 7.0. This behavior does not occur at lower concentrations or higher pH. Arsenic release to solution does not appear to be directly correlated to increasing chlorine concentrations, but is governed by Fe-oxyhydroxide nucleation, which inhibits the release of dissolved arsenic at higher concentrations of chlorine.
- Masters Theses