Tensile behavior of aluminum reinforced with angle-ply boron epoxy laminates

Simple item page
dc.contributor.authorWong, Daniel Ming-Feien
dc.contributor.departmentEngineering Mechanicsen
dc.date.accessioned2014-03-14T21:39:39Zen
dc.date.adate2010-07-07en
dc.date.available2014-03-14T21:39:39Zen
dc.date.issued1974en
dc.date.rdate2010-07-07en
dc.date.sdate2010-07-07en
dc.description.abstractAn experimental investigation of the tensile behavior of aluminum reinforced with angle-ply boron/epoxy laminates was conducted. It is shown that the ultimate stresses of a wide variety of laminate configurations fall within a very narrow range of values. Some configurations of composite reinforced aluminum laminates exhibited higher ultimate stress values than the corresponding all composite laminates while other configurations exhibited lower ultimate stresses than the corresponding all composite laminates. Elastic moduli and Poisson ratios agreed quite well with predicted values but strength predictions were inconsistent.en
dc.description.degreeMaster of Scienceen
dc.format.extent71 leavesen
dc.format.mediumBTDen
dc.format.mimetypeapplication/pdfen
dc.identifier.otheretd-07072010-020249en
dc.identifier.sourceurlhttp://scholar.lib.vt.edu/theses/available/etd-07072010-020249/en
dc.identifier.urihttp://hdl.handle.net/10919/43561en
dc.publisherVirginia Techen
dc.relation.haspartLD5655.V855_1974.W66.pdfen
dc.relation.isformatofOCLC# 21663454en
dc.rightsIn Copyrighten
dc.rights.urihttp://rightsstatements.org/vocab/InC/1.0/en
dc.subject.lccLD5655.V855 1974.W66en
dc.subject.lcshAluminumen
dc.subject.lcshTensile architectureen
dc.titleTensile behavior of aluminum reinforced with angle-ply boron epoxy laminatesen
dc.typeThesisen
dc.type.dcmitypeTexten
thesis.degree.disciplineEngineering Mechanicsen
thesis.degree.grantorVirginia Polytechnic Institute and State Universityen
thesis.degree.levelmastersen
thesis.degree.nameMaster of Scienceen

Files

Original bundle
Now showing 1 - 1 of 1
Thumbnail Image
Name:
LD5655.V855_1974.W66.pdf
Size:
8.45 MB
Format:
Adobe Portable Document Format
Download

Collections

Masters Theses