The Effects of Structure, Humidity and Aging on the Mechanical Properties of Polymeric Ionomers for Fuel Cell Applications

Simple item page
dc.contributor.authorUan-Zo-li, Julie Tammyen
dc.contributor.committeechairKander, Ronald G.en
dc.contributor.committeememberNelson, Douglas J.en
dc.contributor.committeememberLove, Brian J.en
dc.contributor.departmentMaterials Science and Engineeringen
dc.date.accessioned2014-03-14T20:50:15Zen
dc.date.adate2001-12-19en
dc.date.available2014-03-14T20:50:15Zen
dc.date.issued2001-12-04en
dc.date.rdate2002-12-19en
dc.date.sdate2001-12-18en
dc.description.abstractThe purpose of this work was to investigate the effects of structure, humidity and aging on the mechanical behavior of Nafion® and Dais® ionomers. It was determined that the majority of the properties of these membranes were controlled by the formation and growth of the ionic clusters that were the direct result of the ionic nature of these materials. In the process of this study, the properties of Nafion® and sulfonated Dais® polymers were investigated by dynamic mechanical analysis and thermal gravimetric analysis and their water uptake and sorption and desorption isotherms were measured. A mastercurve and a shift factor plot were constructed for 60% sulfonated Dais® membrane. It was determined that an increase in the degree of sulfonation raised the glass transition temperature of these materials by facilitating the formation of the ionic clusters which acted as physical crosslinks, thereby reducing the mobility of polymeric chains. Water was found to effectively plasticize the membranes, especially in the case of Dais® materials, by reducing the storage modulus and decreasing the structural integrity of the ionomers. The effect of pre-treatment of Nafion® was investigated and the glass transition temperature was found to increase as a function of the severity of the treatment procedure. The maximum water uptakes were determined for virgin and aged Nafion® and Dais® membranes and their vapor phase water sorption diffusion coefficients were calculated. The sorption process was found to follow pseudo-Fickian behavior, while the movement of water out of the membranes during the desorption process was determined to be controlled by mechanisms other than diffusion. Lastly, the effect of exposure of Nafion® and 30% sulfonated Dais® membranes to the saturated environment at elevated temperatures was investigated and found to result in the increase in the glass transition temperature of the materials. Results of the exposure effects on the diffusion properties of Nafion® and Dais® were inconclusive. Preliminary findings attributed the changes in the properties of the materials to the counteractive actions of physical aging and the growth of the ionic clusters.en
dc.description.degreeMaster of Scienceen
dc.identifier.otheretd-12182001-152235en
dc.identifier.sourceurlhttp://scholar.lib.vt.edu/theses/available/etd-12182001-152235/en
dc.identifier.urihttp://hdl.handle.net/10919/36259en
dc.publisherVirginia Techen
dc.relation.haspartJTU_thesis.pdfen
dc.rightsIn Copyrighten
dc.rights.urihttp://rightsstatements.org/vocab/InC/1.0/en
dc.subjectPhysical Agingen
dc.subjectDiffusion Propertiesen
dc.subjectFuel Cellen
dc.subjectProton Exchange Membraneen
dc.subjectNafion®en
dc.subjectDais®en
dc.titleThe Effects of Structure, Humidity and Aging on the Mechanical Properties of Polymeric Ionomers for Fuel Cell Applicationsen
dc.typeThesisen
thesis.degree.disciplineMaterials Science and Engineeringen
thesis.degree.grantorVirginia Polytechnic Institute and State Universityen
thesis.degree.levelmastersen
thesis.degree.nameMaster of Scienceen

Files

Original bundle
Now showing 1 - 1 of 1
Thumbnail Image
Name:
JTU_thesis.pdf
Size:
3.61 MB
Format:
Adobe Portable Document Format
Download

Collections

Masters Theses