Friction and degradation of rubber coatings under fretting conditions

Simple item page
dc.contributor.authorVeyret-Abran, Christopheen
dc.contributor.departmentMechanical Engineeringen
dc.date.accessioned2014-03-14T21:40:53Zen
dc.date.adate2010-07-21en
dc.date.available2014-03-14T21:40:53Zen
dc.date.issued1987en
dc.date.rdate2010-07-21en
dc.date.sdate2010-07-21en
dc.description.abstractA fundamental study was conducted to analyze the friction and degradation mechanisms of thin rubber coatings used as fretting corrosion inhibitors. Two elastomers, polyurethane and styreneethylene-butylene (SEBS), were investigated. The mechanisms of wear were studied by analyzing wear scars with optical microscopy. Friction mechanisms were investigated using friction forcedisplacement hysteresis loops and friction force variation with test frequency, fretting amplitude and fIlm thickness. Lastly, coating life variation with these three parameters was studied and explained through a simplified fatigue mechanics approach.en
dc.description.degreeMaster of Scienceen
dc.format.extentxiv, 189 leavesen
dc.format.mediumBTDen
dc.format.mimetypeapplication/pdfen
dc.identifier.otheretd-07212010-020137en
dc.identifier.sourceurlhttp://scholar.lib.vt.edu/theses/available/etd-07212010-020137/en
dc.identifier.urihttp://hdl.handle.net/10919/43827en
dc.publisherVirginia Techen
dc.relation.haspartLD5655.V855_1987.V497.pdfen
dc.relation.isformatofOCLC# 17541460en
dc.rightsIn Copyrighten
dc.rights.urihttp://rightsstatements.org/vocab/InC/1.0/en
dc.subject.lccLD5655.V855 1987.V497en
dc.subject.lcshFretting corrosionen
dc.subject.lcshMechanical wearen
dc.titleFriction and degradation of rubber coatings under fretting conditionsen
dc.typeThesisen
dc.type.dcmitypeTexten
thesis.degree.disciplineMechanical Engineeringen
thesis.degree.grantorVirginia Polytechnic Institute and State Universityen
thesis.degree.levelmastersen
thesis.degree.nameMaster of Scienceen

Files

Original bundle
Now showing 1 - 1 of 1
Thumbnail Image
Name:
LD5655.V855_1987.V497.pdf
Size:
110.55 MB
Format:
Adobe Portable Document Format
Download

Collections

Masters Theses